Mae Tile Ball Clay

Thailand Ball Clay

Chemistry CaO 0.200 K2O 2.200 MgO 0.400 Na2O 0.300 TiO2 0.600 Al2O3 21.100 SiO2 67.500 Fe2O3 1.400

Volatiles LOI 6.300 C 0.300

Links to Other Materials

• Ball Clay - Parent
• Cache

Miscellaneous

• Family: Ball Clay
• Region: None
• Mined At: Unspecified
• Raw Mineral: No
• Generic: No

Notes

Particle Size (e.s.d.)
125 microns - 5.0
20 microns - 91
2 microns - 59
.5 microns - 30
Modulus of Rupture at 110C
Mn/M2 - 2.6
lbf/in2 - 370
Water Absorption
1120C - 3.0
1220C - 0.0
Shrinkage Dry to Fired
1120C - 11.0
1220C - 14.0
Reflectance 464nm
1120C - 45
1220C - 30
Refractoriness
Cone - 29, 1650C

Suppliers

• Claymin (WBB)
  

Authors

• Tony Hansen (Owner)

XML

<?xml version="1.0" encoding="UTF-8"?>
<material name="Mae Tile Ball Clay" descrip="Thailand Ball Clay" generic="0" rawmineral="0" searchkey="" loi="6.60">
<families>
<family name="Ball Clay"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.200" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.400" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="2.200" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.300" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.600" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="21.100" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="67.500" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="1.400" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="6.300" tolerance=""/>
<volatile symbol="" name="" percent="0.300" tolerance=""/>
</volatiles>
<references>
<reference name="seealso" reason=""/>
</references>
<suppliers>
<supplier name="Claymin (WBB)" country="" url="www.wbb.co.uk" label=""/>
</suppliers>
<notes>
<note>Particle Size (e.s.d.)
125 microns - 5.0
20 microns - 91
2 microns - 59
.5 microns - 30
Modulus of Rupture at 110C
Mn/M2 - 2.6
lbf/in2 - 370
Water Absorption
1120C - 3.0
1220C - 0.0
Shrinkage Dry to Fired
1120C - 11.0
1220C - 14.0
Reflectance 464nm
1120C - 45
1220C - 30
Refractoriness
Cone - 29, 1650C
</note>
</notes>
</material>

---

Much more information with complete interlinking to many related databases can be found by logging into the www.ceramicmaterials.info database Copyright 2003 http://digitalfire.com, All Rights Reserved Please support http://ceramicmaterials.info to improve this library

INSIGHT is ceramic chemistry calculation software that runs on Windows, Mac and Linux and talks to this web site.