LM1 Ball Clay
WBB Devon Ball Clay Group 1
Chemistry
|
Volatiles
|
Links to Other Materials
Miscellaneous
- Family: Ball Clay
- Region: None
- Mined At: Unspecified
- Raw Mineral: No
- Generic: No
Notes
Particle Size (e.s.d.)
125 microns - 0.40
10 microns - 98
2 microns - 84
1 microns - 74
Modulus of Rupture at 110C
Mn/M2 - 3.9
lbf/in2 - 570
Defloculant Required - (3:1 Na2SiO3(C.100):Na2CO3) - 0.3
Water Absorption
1120C - 9.0
1220C - 1.00
Shrinkage Dry to Fired
1120C - 14.00
1220C - 17.50
Reflectance 464nm
1120C - 72
1220C - 57
Refractoriness
Cone - 33, 1730C
Suppliers
- WBB
Authors
- Tony Hansen (Owner)
XML
<?xml version="1.0" encoding="UTF-8"?>
<material name="LM1 Ball Clay" descrip="WBB Devon Ball Clay Group 1" generic="0" rawmineral="0" searchkey="" loi="14.20">
<families>
<family name="Ball Clay"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.100" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.300" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="1.800" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.200" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.900" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="33.900" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="49.400" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="1.000" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="12.400" tolerance=""/>
<volatile symbol="" name="" percent="1.800" tolerance=""/>
</volatiles>
<references>
<reference name="seealso" reason=""/>
</references>
<suppliers>
<supplier name="WBB" country="UK" url="www.wbb.co.uk" label=""/>
</suppliers>
<notes>
<note>Particle Size (e.s.d.)
125 microns - 0.40
10 microns - 98
2 microns - 84
1 microns - 74
Modulus of Rupture at 110C
Mn/M2 - 3.9
lbf/in2 - 570
Defloculant Required - (3:1 Na2SiO3(C.100):Na2CO3) - 0.3
Water Absorption
1120C - 9.0
1220C - 1.00
Shrinkage Dry to Fired
1120C - 14.00
1220C - 17.50
Reflectance 464nm
1120C - 72
1220C - 57
Refractoriness
Cone - 33, 1730C</note>
</notes>
</material>