Huntingdon Ball Clay

Tennessee Ball Clay

Chemistry

CaO	0.100
K2O	0.100
MgO	0.100
Na2O	0.100
TiO2	2.400
Al2O3	38.300
SiO2	44.800
Fe2O3	0.600

Volatiles

LOI	13.600
C	0.300

Links to Other Materials

Ball Clay - Parent
Cache

Miscellaneous

Family: Ball Clay
Region: None
Mined At: Unspecified
Raw Mineral: No
Generic: No

Notes

Modulus of Rupture at 110C
Mn/M2 - 2.6
lbf/in2 - 370
Water Absorption
1120C - 13.0
1220C - 8.0
Shrinkage Dry to Fired
1120C - 8.0
1220C - 12.5
Refractoriness
Cone - 35, 1770C

Data

% < 0.5 microns: 44
% < 1 micron: 60
% < 10 microns: 95
% < 2 microns: 71
% < 20 microns: 97
% < 5 microns: 90
PCE: 35

Suppliers

United Clays (WBB)

Authors

Tony Hansen (Owner)

XML

<?xml version="1.0" encoding="UTF-8"?>
<material name="Huntingdon Ball Clay" descrip="Tennessee Ball Clay" generic="0" rawmineral="0" searchkey="" loi="13.90">
<families>
<family name="Ball Clay"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.100" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.100" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="0.100" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.100" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="2.400" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="38.300" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="44.800" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="0.600" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="13.600" tolerance=""/>
<volatile symbol="" name="" percent="0.300" tolerance=""/>
</volatiles>
<references>
<reference name="seealso" reason=""/>
</references>
<suppliers>
<supplier name="United Clays (WBB)" country="" url="" label=""/>
</suppliers>
<notes>
<note>Modulus of Rupture at 110C
Mn/M2 - 2.6
lbf/in2 - 370
Water Absorption
1120C - 13.0
1220C - 8.0
Shrinkage Dry to Fired
1120C - 8.0
1220C - 12.5
Refractoriness
Cone - 35, 1770C
</note>
</notes>
<testdata>
<testitem testname="1" value="44"/>
<testitem testname="1" value="60"/>
<testitem testname="1" value="95"/>
<testitem testname="1" value="71"/>
<testitem testname="1" value="97"/>
<testitem testname="1" value="90"/>
<testitem testname="1" value="35"/>
</testdata>
</material>

Much more information with complete interlinking to many related
databases can be found by logging into the www.ceramicmaterials.info database

INSIGHT is ceramic chemistry
calculation software that runs on
Windows, Mac and Linux and talks
to this web site.

Ceramic Materials Database