No. 1 Ball Clay

Chemistry

CaO	0.100
K2O	1.001
MgO	0.100
Na2O	0.100
TiO2	0.701
Al2O3	30.631
SiO2	54.555
Fe2O3	1.001

Volatiles

LOI	10.900
C	0.900

Links to Other Materials

Ball Clay - Parent
Cache

Miscellaneous

Family: Ball Clay
Region: None
Mined At: Unspecified
Raw Mineral: No
Generic: No

Notes

Particle Size (e.s.d.)
125 microns - 0.1
20 microns - 95
2 microns - 65
.5 microns - 52
Modulus of Rupture at 110C
Mn/M2 - 9.8
lbf/in2 - 1420
Water Absorption
1120C - 13.0
1220C - 6.0
Shrinkage Dry to Fired
1120C - 8.0
1220C - 12.0
Reflectance 464nm
1120C - 68
1220C - 67
Refractoriness
Cone - 33, 1730C

Suppliers

Clay Orient (WBB)

Authors

Tony Hansen (Owner)

XML

<?xml version="1.0" encoding="UTF-8"?>
<material name="No. 1 Ball Clay" descrip="" generic="0" rawmineral="0" searchkey="" loi="11.80">
<families>
<family name="Ball Clay"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.100" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.100" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="1.001" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.100" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.701" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="30.631" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="54.555" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="1.001" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="10.900" tolerance=""/>
<volatile symbol="" name="" percent="0.900" tolerance=""/>
</volatiles>
<references>
<reference name="seealso" reason=""/>
</references>
<suppliers>
<supplier name="Clay Orient (WBB)" country="" url="" label=""/>
</suppliers>
<notes>
<note>Particle Size (e.s.d.)
125 microns - 0.1
20 microns - 95
2 microns - 65
.5 microns - 52
Modulus of Rupture at 110C
Mn/M2 - 9.8
lbf/in2 - 1420
Water Absorption
1120C - 13.0
1220C - 6.0
Shrinkage Dry to Fired
1120C - 8.0
1220C - 12.0
Reflectance 464nm
1120C - 68
1220C - 67
Refractoriness
Cone - 33, 1730C</note>
</notes>
</material>

Much more information with complete interlinking to many related
databases can be found by logging into the www.ceramicmaterials.info database

INSIGHT is ceramic chemistry
calculation software that runs on
Windows, Mac and Linux and talks
to this web site.

Ceramic Materials Database