CC China Clay

Devon China Clay

Chemistry

CaO	0.100
K2O	2.400
MgO	0.200
Na2O	0.100
TiO2	0.200
Al2O3	37.300
SiO2	47.000
Fe2O3	0.800

Volatiles

LOI

12.000

Links to Other Materials

Kaolin - Parent
Cache

Miscellaneous

Family: Kaolin
Region: None
Mined At: Unspecified
Raw Mineral: No
Generic: No

Notes

Particle Size (e.s.d.)
125 microns - <0.03
10 microns - 96
2 microns - 51
1 microns - 35
Modulus of Rupture at 110C
Mn/M2 - 1.0
lbf/in2 - 140
Defloculant Required - (3:1 Na2SiO3(C.100):Na2CO3) - 0.0
Water Absorption
1120C - 20.5
1220C - 7.00
Shrinkage Dry to Fired
1120C - 9.50
1220C - 18.50
Reflectance 464nm
1120C - 86
1220C - 84
Refractoriness
Cone - 33, 1730C

Suppliers

Devon China (WBB)

Authors

Tony Hansen (Owner)

XML

<?xml version="1.0" encoding="UTF-8"?>
<material name="CC China Clay" descrip="Devon China Clay" generic="0" rawmineral="0" searchkey="" loi="12.00">
<families>
<family name="Kaolin"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.100" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.200" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="2.400" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.100" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.200" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="37.300" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="47.000" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="0.800" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="12.000" tolerance=""/>
</volatiles>
<references>
<reference name="seealso" reason=""/>
</references>
<suppliers>
<supplier name="Devon China (WBB)" country="" url="" label=""/>
</suppliers>
<notes>
<note>Particle Size (e.s.d.)
125 microns - <0.03
10 microns - 96
2 microns - 51
1 microns - 35
Modulus of Rupture at 110C
Mn/M2 - 1.0
lbf/in2 - 140
Defloculant Required - (3:1 Na2SiO3(C.100):Na2CO3) - 0.0
Water Absorption
1120C - 20.5
1220C - 7.00
Shrinkage Dry to Fired
1120C - 9.50
1220C - 18.50
Reflectance 464nm
1120C - 86
1220C - 84
Refractoriness
Cone - 33, 1730C</note>
</notes>
</material>

Much more information with complete interlinking to many related
databases can be found by logging into the www.ceramicmaterials.info database

INSIGHT is ceramic chemistry
calculation software that runs on
Windows, Mac and Linux and talks
to this web site.

Ceramic Materials Database