Caroso FC Ball Clay
Devon Composite Ball Clay Blend
Chemistry
|
Volatiles
|
Links to Other Materials
Miscellaneous
- Family: Ball Clay
- Region: None
- Mined At: Unspecified
- Raw Mineral: No
- Generic: No
Notes
Particle Size (e.s.d.)
125 microns - 0.80
10 microns - 97
2 microns - 78
1 microns - 67
Modulus of Rupture at 110C
Mn/M2 - 6.2
lbf/in2 - 900
Defloculant Required - (3:1 Na2SiO3(C.100):Na2CO3) - 0.3
Water Absorption
1120C - 4.0
1220C - 0.50
Shrinkage Dry to Fired
1120C - 12.00
1220C - 14.00
Reflectance 464nm
1120C - 68
1220C - 48
Refractoriness
Cone - 33, 1730C
Suppliers
- WBB
Authors
- Tony Hansen (Owner)
XML
<?xml version="1.0" encoding="UTF-8"?>
<material name="Caroso FC Ball Clay" descrip="Devon Composite Ball Clay Blend" generic="0" rawmineral="0" searchkey="" loi="9.90">
<families>
<family name="Ball Clay"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.100" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.299" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="2.292" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.299" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="1.296" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="29.004" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="55.914" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="0.897" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="9.600" tolerance=""/>
<volatile symbol="" name="" percent="0.299" tolerance=""/>
</volatiles>
<references>
<reference name="seealso" reason=""/>
</references>
<suppliers>
<supplier name="WBB" country="UK" url="www.wbb.co.uk" label=""/>
</suppliers>
<notes>
<note>Particle Size (e.s.d.)
125 microns - 0.80
10 microns - 97
2 microns - 78
1 microns - 67
Modulus of Rupture at 110C
Mn/M2 - 6.2
lbf/in2 - 900
Defloculant Required - (3:1 Na2SiO3(C.100):Na2CO3) - 0.3
Water Absorption
1120C - 4.0
1220C - 0.50
Shrinkage Dry to Fired
1120C - 12.00
1220C - 14.00
Reflectance 464nm
1120C - 68
1220C - 48
Refractoriness
Cone - 33, 1730C</note>
</notes>
</material>