Plastic Mix 381
SPOUT, LADLE LINING GRAPHITE CLAY
Chemistry
|
Miscellaneous
- Family: Clay Other
- Region: None
- Mined At: Unspecified
- Raw Mineral: No
- Generic: No
Notes
High silica, air and heat bonded plastic refractory with graphite
It has been specially designed to resist penetration and erosion by highly acidic, iron rich slags or iron rich mattes. In a 'high workability' version, it can also be used as a thin, expendable lining for iron ladles or for repairing spouts and lips of these ladles.
Maximum service temperature: 2750F (1510C)
Dry Shrinkage 220F: 0.1-1.5% 2550F: 0.0-1.5% 2750F: 1.0-4.0%
Hot load test ASTM C16 (Dried by not previously fired): 2-5%
Panel spalling test ASTM C180 (preheated at 2750F spalling loss): 0-1%
Modulus of Rupture ASTM C491
(Dried at 220F): 50-100 in/square in (0.34-0.69 MPa)
(Heated at 1500F and cooled): 20-40 in/sq in (0.14-0.28 MPa)
(Heated at 2000F and cooled): 80-120 (0.55-0.82)
Thermal Conductivity
400F: 0.21 W/(m.K)
800F: 0.24 "
1200F: 0.28
1600F: 0.31
2000F: 0.35
Suppliers
- A. P. Green
Authors
- Tony Hansen (Owner)
XML
<?xml version="1.0" encoding="UTF-8"?>
<material name="Plastic Mix 381" descrip="SPOUT, LADLE LINING GRAPHITE CLAY" generic="0" rawmineral="0" searchkey="" loi="0.00">
<families>
<family name="Clay Other"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.350" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.350" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="0.550" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.550" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.750" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="8.500" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="88.500" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="0.750" tolerance=""/>
</oxides>
<suppliers>
<supplier name="A. P. Green" country="" url="" label=""/>
</suppliers>
<notes>
<note>High silica, air and heat bonded plastic refractory with graphite
It has been specially designed to resist penetration and erosion by highly acidic, iron rich slags or iron rich mattes. In a \'high workability\' version, it can also be used as a thin, expendable lining for iron ladles or for repairing spouts and lips of these ladles.
Maximum service temperature: 2750F (1510C)
Dry Shrinkage 220F: 0.1-1.5% 2550F: 0.0-1.5% 2750F: 1.0-4.0%
Hot load test ASTM C16 (Dried by not previously fired): 2-5%
Panel spalling test ASTM C180 (preheated at 2750F spalling loss): 0-1%
Modulus of Rupture ASTM C491
(Dried at 220F): 50-100 in/square in (0.34-0.69 MPa)
(Heated at 1500F and cooled): 20-40 in/sq in (0.14-0.28 MPa)
(Heated at 2000F and cooled): 80-120 (0.55-0.82)
Thermal Conductivity
400F: 0.21 W/(m.K)
800F: 0.24 "
1200F: 0.28
1600F: 0.31
2000F: 0.35</note>