Ceramic Materials Database

Go to Oxides Materials Articles Glossary
CeramicMaterials.Info Database

NT/BKS Brick Clay

Brick Clay Blend

Chemistry CaO 0.200 K2O 2.300 MgO 0.400 Na2O 0.400 TiO2 1.300 Al2O3 24.200 SiO2 63.200 Fe2O3 1.000

Volatiles LOI 7.000 C 1.700

Miscellaneous

• Family: Clay Other
• Region: None
• Mined At: Unspecified
• Raw Mineral: No
• Generic: No

Notes

Particle Size (e.s.d.)
125 microns - 2.00
10 microns - 91
2 microns - 73
1 microns - 57
Modulus of Rupture at 110C
Mn/M2 - 7.6
lbf/in2 - 1110
Water Absorption
1120C - 2.5
1220C - 5.00
Shrinkage Dry to Fired
1120C - 8.50
1220C - 11.50
Refractoriness
Cone - 28, 1630C

Suppliers

• WBB
  

Authors

• Tony Hansen (Owner)

XML

<?xml version="1.0" encoding="UTF-8"?>
<material name="NT/BKS Brick Clay" descrip="Brick Clay Blend" generic="0" rawmineral="0" searchkey="" loi="8.70">
<families>
<family name="Clay Other"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.200" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.400" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="2.300" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.400" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="1.300" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="24.200" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="63.200" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="1.000" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="7.000" tolerance=""/>
<volatile symbol="" name="" percent="1.700" tolerance=""/>
</volatiles>
<suppliers>
<supplier name="WBB" country="UK" url="www.wbb.co.uk" label=""/>
</suppliers>
<notes>
<note>Particle Size (e.s.d.)
125 microns - 2.00
10 microns - 91
2 microns - 73
1 microns - 57
Modulus of Rupture at 110C
Mn/M2 - 7.6
lbf/in2 - 1110
Water Absorption
1120C - 2.5
1220C - 5.00
Shrinkage Dry to Fired
1120C - 8.50
1220C - 11.50
Refractoriness
Cone - 28, 1630C</note>
</notes>
</material>

---