NSC Kaolin
Chemistry
|
Volatiles
|
Links to Other Materials
- Grolleg Kaolin - Unspecified
- NSC Kaolin - Unspecified
- Remblend Kaolin - Unspecified
- Treviscoe Kaolin - Unspecified
- Standard Porcelain Kaolin - Unspecified
- Super Standard Porcelain - Unspecified
- English Kaolin - Parent
- Kaolin - Parent
- Cache
Miscellaneous
- Family: Kaolin
- Region: None
- Mined At: Unspecified
- Raw Mineral: No
- Generic: No
Notes
Particle Size Distribution:
>53 microns: 0.05 max
>10 microns: 16
<2 microns: 40
Modulus of Rupture, Kgf/cm2:
At 80% Relative Humidity: 8.0
Dried at 110C: 16.2
Casting Rate @ 69% solids (mm2/min): 1.0
% P84 Deflocculant Required for 5 Poise Slip: 0.5
1180C 1280C
Fired Absorption: 16% 8%
Fired Shrinkage: 7% 11%
Brightness: 85 85
Suppliers
- ECC
- Imerys
Authors
- Tony Hansen (Owner)
XML
<?xml version="1.0" encoding="UTF-8"?>
<material name="NSC Kaolin" descrip="" generic="0" rawmineral="0" searchkey="" loi="11.90">
<families>
<family name="Kaolin"/>
</families>
<oxides>
<oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.050" tolerance=""/>
<oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.300" tolerance=""/>
<oxide symbol="K2O" name="Potassium Oxide" status="" percent="2.100" tolerance=""/>
<oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.100" tolerance=""/>
<oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.040" tolerance=""/>
<oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="37.000" tolerance=""/>
<oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="48.000" tolerance=""/>
<oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="0.800" tolerance=""/>
</oxides>
<volatiles>
<volatile symbol="" name="" percent="11.900" tolerance=""/>
</volatiles>
<references>
<reference name="seealso" reason=""/>
<reference name="seealso" reason=""/>
<reference name="seealso" reason=""/>
<reference name="seealso" reason=""/>
<reference name="seealso" reason=""/>
<reference name="seealso" reason=""/>
<reference name="seealso" reason=""/>
<reference name="seealso" reason=""/>
</references>
<suppliers>
<supplier name="ECC" country="UK" url="www.ecci.co.uk" label=""/>
<supplier name="Imerys" country="FR" url="http://www.imerys.com" label=""/>
</suppliers>
<notes>
<note>Particle Size Distribution:
>53 microns: 0.05 max
>10 microns: 16
<2 microns: 40
Modulus of Rupture, Kgf/cm2:
At 80% Relative Humidity: 8.0
Dried at 110C: 16.2
Casting Rate @ 69% solids (mm2/min): 1.0
% P84 Deflocculant Required for 5 Poise Slip: 0.5
1180C 1280C
Fired Absorption: 16% 8%
Fired Shrinkage: 7% 11%
Brightness: 85 85</note>
</notes>
</material>
Much more information with complete interlinking to many related Copyright 2003 http://digitalfire.com, All Rights Reserved Please support http://ceramicmaterials.info to improve this library |  |